| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 成形收缩率 | 流动方向，- | ASTM D955 | 0.1-0.4 | % |
| 垂直方向，- | ASTM D955 | 0.8-1.1 | % | ||
| 比重 | ASTM D792 | 1.62-1.68 | |||
| 吸水率 | 24hr immersion | ASTM D570 | 0.03 | % | |
| 玻璃纤维含量 | Ash | 30 | % | ||
| 机械性能 | IZOD冲击强度 | 切口1/4″ | ASTM D256 | 7-13 | kg-cm/cm |
| 引张强度 | ASTM D638 | 1100-1400 | kg/cm | ||
| 硬度 | ASTM D785 | 94 | M-Scale | ||
| 挠曲强度 | ASTM D790 | 1500-2300 | kg/cm | ||
| 引张伸长率 | ASTM D638 | 2.5-4.5 | % | ||
| 挠曲弹性率 | ASTM D790 | ≥70000 | kg/cm | ||
| 电气性能 | 诱电正接 | ASTM D150 | 0.001 | 60Hz | |
| 耐电弧性 | ASTM D495 | 100 | sec | ||
| 绝缘破坏强度 | 2mm | ASTM D149 | ＞20 | KV/mm | |
| 体积抵抗率 | ASTM D257 | ＞10 | Ω-cm | ||
| 表面抵抗率 | ASTM D257 | ＞10 | Ω | ||
| 诱电率 | ASTM D150 | 3 | 60Hz | ||
| 热性能 | 耐燃性 | 0.8mm | UL94 | V-0 | |
| 融点 | DSC | 225 | ℃ | ||
| 线膨胀系数 | ASTM D696 | 3 | 10 | ||
| 热变形温度 | 18.6kg/cm | ASTM D648 | 208（220） | ℃ | |
PBT/台湾长春/4130 玻纤增强30% 阻燃级